The chemical composition and processing properties of 6060 and 6063 aluminum alloys are similar, but not identical. The difference between the two is strength. 6060 is the national standard aluminum alloy for doors and windows, and 6063 is the aerospace aluminum alloy approved by the state.

aluminium 6063.

6060 aluminum material composition

Si: 0.3-0.6Fe: 0.1-0.3Cu: 0.1Mn: 0.1Mg: 0.35-0.6Cr: – Zn: 0.1 Other: – Ti: 0.15 Other total: 0.15Al: balance

Performance:

Tensile strength σb (MPa): ≥ 470

Conditional yield strength σ0.2 (MPa): ≥420

Elongation δ5 (%): ≥ 6

Features:

1. High strength heat treatable alloy.

2. Good mechanical properties.

3. Good usability.

4. Easy to process and good wear resistance.

5. Anti-corrosion performance, good oxidation resistance

Main uses: Aerospace fixtures, trucks, tower buildings, boats, pipelines and other areas of construction that require strength, weldability and corrosion resistance.

Such as: aircraft parts, camera lenses, couplers, marine machining aluminium accessories and hardware, electronic accessories and connectors, decorative or various hardware, hinged heads, magnetic heads, brake pistons, hydraulic pistons, electrical accessories, valves and valve parts.

6063 aluminum alloy chemical composition

Aluminum Al: balance silicon Si: 0.20-0.6 copper Cu: ≤ 0.10 magnesium Mg: 0.45-0.9 zinc Zn: ≤ 0.10 manganese Mn: ≤ 0.10 titanium Ti: ≤ 0.10 chromium Cr: ≤ 0.10 iron Fe: 0.000 ~ 0.350 Note: Single: ≤ 0.05; total: ≤ 0.15

The density of 6063 is 2.69g/cm3

Physical and mechanical properties:

Tensile strength σb (MPa): ≥ 205 condition Yield strength σ0.2 (MPa): ≥ 170 elongation δ5 (%): ≥ 96063 aluminum plate product features Description:

6063 aluminum alloy belongs to Al-Mg-Si alloy and has a wide range of applications. Especially in the construction industry, it is inseparable from this alloy and is a promising alloy. Good corrosion resistance, excellent weldability, good cold workability and medium strength.

The main alloying elements are magnesium and silicon, which have excellent processing properties, excellent weldability, extrusion and electroplating properties, good corrosion resistance, toughness, easy polishing, color film, excellent anodizing effect, and are typical. Extruded alloy. 6063 aluminum alloy profiles are widely used in architectural profiles, irrigation pipes, vehicles, gantry, furniture, etc. due to their good plasticity, moderate heat treatment strength, good welding performance and gorgeous color on the surface after anodizing. Pipes, rods and profiles for elevators, fences, etc.

It is a low alloyed Al-Mg-Si high plasticity alloy. Has many valuable features: 1. Heat treatment strengthening, high impact toughness, can not be sensitive to lack of. 2. It has excellent thermoplasticity and can be extruded at high speed into a complex structure. Thin wall. Hollow various profiles or forged forgings with complex structure, wide quenching temperature range, low quenching sensitivity, after extrusion and forging demoulding, As long as the temperature is higher than the quenching temperature. That is, it can be quenched by spraying water or water. Thin-walled parts (6<3mm) can also be subjected to wind quenching. 3. Excellent welding performance and corrosion resistance, no stress corrosion cracking tendency. In the heat-treated reinforced aluminum alloy, the Al-Mg-Si alloy is an alloy in which stress corrosion cracking is not observed. 4. The surface after processing is very smooth and easy to anodize and color. The disadvantage is that if it is aged at room temperature for a period of time after quenching, it will have an adverse effect on the strength (parking effect).